3 May 2017 Minority carrier diffusion lengths and mobilities in low-doped n-InGaAs for focal plane array applications
Author Affiliations +
The hole diffusion length in n-InGaAs is extracted for two samples of different doping concentrations using a set of long and thin diffused junction diodes separated by various distances on the order of the diffusion length. The methodology is described, including the ensuing analysis which yields diffusion lengths between 70 - 85 μm at room temperature for doping concentrations in the range of 5 − 9 × 1015 cm−3 . The analysis also provides insight into the minority carrier mobility which is a parameter not commonly reported in the literature. Hole mobilities on the order of 500 − 750 cm2/V·s are reported for the aforementioned doping range, which are comparable albeit longer than the majority hole mobility for the same doping magnitude in p-InGaAs. A radiative recombination coefficient of (0.5±0.2)×10−10 cm−3 s −1 is also extracted from the ensuing analysis for an InGaAs thickness of 2.7 μm. Preliminary evidence is also given for both heavy and light hole diffusion. The dark current of InP/InGaAs p-i-n photodetectors with 25 and 15 μm pitches are then calibrated to device simulations and correlated to the extracted diffusion lengths and doping concentrations. An effective Shockley-Read-Hall lifetime of between 90-200 μs provides the best fit to the dark current of these structures.
© (2017) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Alexandre W. Walker and Mike W. Denhoff "Minority carrier diffusion lengths and mobilities in low-doped n-InGaAs for focal plane array applications", Proc. SPIE 10177, Infrared Technology and Applications XLIII, 101772D (3 May 2017);


Contact property of Ni(Ti)/Pt/Au on p-In0.52Al0.48As
Proceedings of SPIE (October 15 2012)
1/f noise in Hg1-xCdxTe detectors
Proceedings of SPIE (August 05 2002)

Back to Top