10 February 2017 Comparative analysis of luminescent properties of Nd3+/Yb3+ codoped optical fibers
Author Affiliations +
Proceedings Volume 10325, Optical Fibers and Their Applications 2017; 1032503 (2017)
Event: 17th Conference on Optical Fibres and Their Applications, 2017, Supraśl, Poland, Poland
In this article the luminescence properties of three different constructions of doble-clad optical fibers with multicores co-doped with Nd/Yb ions have been investigated. All fibers were made with thermally stable aluminosilicate glass. In each optical fiber, strong and wide emission in the 1μm range obtained by Nd3+ → Yb3+ energy transfer corresponding to the superposition of radiative transitions in two relaxation channels at 1062 nm (Nd3+: 4F3/24I11/2 ) and at 980 nm (Yb3+2: F5/22F7/2 ) was observed. Optimization of doping system, geometry and amount of cores in fabricated optical fibers shows the possibility of controlling the luminescence shape achieved directly from the end of fiber. Comparative analysis of shape of luminescence (λexc = 808 nm) obtained in fabricated optical fibers and amplified spontaneous emission were also discussed.
© (2017) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Jacek Zmojda, Marcin Kochanowicz, Piotr Miluski, Tomasz Ragin, Dominik Dorosz, Jan Dorosz, and Andrzej Zając "Comparative analysis of luminescent properties of Nd3+/Yb3+ codoped optical fibers", Proc. SPIE 10325, Optical Fibers and Their Applications 2017, 1032503 (10 February 2017);