Laser damage of optical windows with random antireflective surface structures on both interfaces

Christopher R. Wilson; Matthew G. Potter; Lynda E. Busse; Jesse A Frantz; L. Brandon Shaw; Jas S. Sanghera; Ishwar D. Aggarwal; Menelaos K. Poutous

doi:10.1117/12.2279614

13 November 2017 Laser damage of optical windows with random antireflective surface structures on both interfaces

Christopher R. Wilson, Matthew G. Potter, Lynda E. Busse, Jesse A Frantz, L. Brandon Shaw, Jas S. Sanghera, Ishwar D. Aggarwal, Menelaos K. Poutous

Author Affiliations +

Proceedings Volume 10447, Laser-Induced Damage in Optical Materials 2017; 1044706 (2017) https://doi.org/10.1117/12.2279614
Event: SPIE Laser Damage, 2017, Boulder, Colorado, United States

Abstract

High average-power, nanosecond-duration, laser pulses induce damage on uncoated optics, due in part to an enhanced localized field at the exit surface of the components. Similarly, anti-reflection (AR) thin-film coated optics have similar field enhancement regions, due to multiple boundaries, and experience laser induced damage on both entry and exit interfaces. Sub-wavelength anti-reflection randomly structured surfaces (rARSS) have been shown to have a higher laser-induced damage threshold than traditional AR coatings. Previously published work detailed laser-induced damage on rARSS on a single surface of optical quality, planar, fused silica substrates; optimized for maximum transmission (99.5%) at 1064 nm. The present study explores the introduction of rARSS to both sides of the substrate. Laser-induced damage was systematically created and measured at contiguous locations along the substrate, using 1064 nm wavelength, 6-10 ns duration pulses. Laser output was focused to increase incident irradiance at the initial interface. Incident fluence was directly controlled by Q-switching the laser to create fluence values at, and above, damage thresholds for both entry and exit sides. It was determined that double-sided rARSS substrates have a higher damage threshold than thin-film AR coatings, while they have a lower damage threshold than entrance-only and exit-only sided rARSS (previous study), as well as, lower damage threshold than plain, optical quality, uncoated, fused silica. Damage on the exit-side of the substrate was ballistic in nature, showing surface cracks and outward-oriented debris craters. Contrastingly, damage on the entry-side of the substrate was thermally-induced local-densification of random structures with a latent footprint.

Citation Download Citation

Christopher R. Wilson, Matthew G. Potter, Lynda E. Busse, Jesse A Frantz, L. Brandon Shaw, Jas S. Sanghera, Ishwar D. Aggarwal, and Menelaos K. Poutous "Laser damage of optical windows with random antireflective surface structures on both interfaces", Proc. SPIE 10447, Laser-Induced Damage in Optical Materials 2017, 1044706 (13 November 2017); https://doi.org/10.1117/12.2279614

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

;

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE