1 September 1991 Thick, fine-grained beryllium optical coatings
Author Affiliations +
Abstract
Fine grained, sputter-deposited Be coatings with thicknesses up to 290 microns have been laid down on six coupons of various substrate materials including S-200 grade beryllium, SiC and Ti6Al4V alloy. Each coated substrate was subsequently polished to a very low surface roughness (less than 5 A rms) finish by one of two different polishing techniques. Bidirectional reflectance distribution function (BRDF) measurements were taken at 632.8 nm and at 10.6 microns. BRDF values at 10.6 microns were measured as low as 9 x 10 exp -7/sr at 10-deg off-specular. Calculated power spectrum density curves showed remarkably little or no anomalous scatter except for one coating laid down with no substrate bias and an uncooled substrate. The measured reflectances of the polished Be coatings at 10.6 microns is about 5 percent below that for the gold reference surface (i.e., about 94 percent of absolute reflectance).
© (1991) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Brian W. Murray, Eric Ulph Sr., and Peter N. Richard "Thick, fine-grained beryllium optical coatings", Proc. SPIE 1485, Reflective and Refractive Optical Materials for Earth and Space Applications, (1 September 1991); https://doi.org/10.1117/12.46528
PROCEEDINGS
10 PAGES


SHARE
Advertisement
Advertisement
RELATED CONTENT

SiC coatings on RB SiC mirrors for ultrasmooth surfaces
Proceedings of SPIE (December 06 1993)
Protected silver coatings for low scatter SiC and SiC Si...
Proceedings of SPIE (December 12 2003)
High-reflectance coatings for space applications in the EUV
Proceedings of SPIE (January 21 1993)
CVC silicon carbide high-performance optical systems
Proceedings of SPIE (October 14 2004)
Surface modification of SiC mirror by IARE method
Proceedings of SPIE (February 18 2011)

Back to Top