12 November 1999 Multiwavelength lasers fabricated by a novel impurity-free quantum-well intermixing technology
Author Affiliations +
Proceedings Volume 3896, Design, Fabrication, and Characterization of Photonic Devices; (1999) https://doi.org/10.1117/12.370306
Event: International Symposium on Photonics and Applications, 1999, Singapore, Singapore
Abstract
Using impurity free vacancy enhanced disordering (IFVD), the shift in the band gap of Al0.3Ga0.7As/GaAs QW structures can be precisely controlled by an Al layer buried between a spin-on silica film and wet-oxidized GaAs surface. The blue shift in wavelength of Al0.3Ga0.7As/GaAs QW photoluminescence (PL) depends linearly on the thickness of the buried Al layer. By changing the Al layer thickness, the PL peak wavelength can be tuned from 7870 angstrom for the as-grown sample to 7300 angstrom and 7050 angstrom after 20s and 45s rapid thermal annealing at 850°C respectively. Applying this technology, three wavelength lasers were successfully fabricated in a single chip. The laser is a GaAs/Al0.3Ga0.7As three quantum well GRIN-SCH structure. Al layers with different thickness, i.e., no Al, 200 angstrom and 300 angstrom thick respectively, were buried between the oxidized GaAs surface and the silica film by two step photo-lithography and lift- off in three adjacent regions with 200 μm spacing. After one step rapid thermal annealing, the wafer was processed into 6 μm oxide-strip lasers. At room temperature the intermixed lasers covered with different thickness of Al layer show different lasing wavelengths. All the lasers have similar threshold current and slope efficiency.
© (1999) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
JingHua Teng, Soo-Jin Chua, Y. H. Huang, Zhenhua Zhang, G. Li, A. Saher Helmy, and John H. Marsh "Multiwavelength lasers fabricated by a novel impurity-free quantum-well intermixing technology", Proc. SPIE 3896, Design, Fabrication, and Characterization of Photonic Devices, (12 November 1999); https://doi.org/10.1117/12.370306