11 March 2002 Loading effect parameters of dry etcher system and their analysis in mask-to-mask loading and within-mask loading
Author Affiliations +
Abstract
The Cr etch rate is affected by Cr density to be etched at the photomask. Different mask-to-mask and within-mask pattern densities have made difficult to control the final CD. We have tested loading effect using binary Cr mask with ZEP7000 photoresist. The loading effect was evaluated for the masks fabricated at the various dry etch conditions with different within-mask Cr loading. The Cr etch rate and selectivity was observed at various process conditions and relations between parameters of dry etch process and Cr loading were evaluated. The horizontal and the vertical Cr etch rates were investigated and the process parameter dependence on the Cr loading was analyzed. The horizontal and the vertical photoresist etch rates were evaluated for the photoresist loading effect. The cause of mask-to-mask loading and within-mask loading are mainly from Cr loading and photoresists loading, respectively. The Cr loading is mainly affected by source power, pressure, and Cl2/O2 ratio. In our system, within-mask Cr loading is strongly dependent on the process parameters when the selectivity of Cr to PR is below 1. If uniformity and selectivity are acceptable, high DC bias, high ga flow, low pressure, and high Cl2/O2 ratio are recommended to reduce loading effect.
© (2002) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Hyuk-Joo Kwon, Dong-Soo Min, Pil-Jin Jang, Byung-Soo Chang, Boo-Yeon Choi, and Soo-Hong Jeong "Loading effect parameters of dry etcher system and their analysis in mask-to-mask loading and within-mask loading", Proc. SPIE 4562, 21st Annual BACUS Symposium on Photomask Technology, (11 March 2002); https://doi.org/10.1117/12.458353
PROCEEDINGS
9 PAGES


SHARE
Advertisement
Advertisement
RELATED CONTENT

Plasma etch of Cr masks utilizing TCP source for a...
Proceedings of SPIE (August 16 2002)
Dry etching of Cr layer and its loading effect
Proceedings of SPIE (September 05 2001)
65 nm node photomask etching with zero CD process bias
Proceedings of SPIE (November 04 2005)
Plasma etch of binary Cr masks CD uniformity study...
Proceedings of SPIE (December 30 1999)
Achieving 65 nm design rule dry etch performance a...
Proceedings of SPIE (August 20 2004)

Back to Top