Process development of 6-in EUV mask with TaBN absorber

Tsutomu Shoki; Morio Hosoya; Takeru Kinoshita; Hideo Kobayashi; Youichi Usui; Ryo Ohkubo; Shinichi Ishibashi; Osamu Nagarekawa

doi:10.1117/12.477007

1 August 2002 Process development of 6-in EUV mask with TaBN absorber

Tsutomu Shoki, Morio Hosoya, Takeru Kinoshita, Hideo Kobayashi, Youichi Usui, Ryo Ohkubo, Shinichi Ishibashi, Osamu Nagarekawa

Author Affiliations +

Proceedings Volume 4754, Photomask and Next-Generation Lithography Mask Technology IX; (2002) https://doi.org/10.1117/12.477007
Event: Photomask and Next Generation Lithography Mask Technology IX, 2002, Yokohama, Japan

Abstract

6-inch EUV masks consisting of Mo/Si multilayers and patterned CrX buffer and TaBN absorber layers have recently been developed and evaluated. Mo/Si multilayers with a relatively high EUV reflectivity of 66 percent and an excellent uniformity were obtained on the polished ULE substrates by an ion beam sputtering method. The multilayers showed high durability to the acid abased cleaning and baking at 150 degrees C used in the conventional mask-making process. The Cr based film was optimized as a repair buffer to obtain a high reflectivity of 52 percent at 257 nm and low stress within 100 MPa. TaBN absorbers with a low reflectivity were obtained by optimizing the film compositions, which resulted in a high image contrast to the multilayer for DUV inspection. An EUV contrast level of 99 percent was achieved for a thinner, 100-nm thick absorber stack. Using the optimized mask process, EUV mask with patterns of 180-nm width were successfully obtained, without a significant drop in EUV reflectivity.

Citation Download Citation

Tsutomu Shoki, Morio Hosoya, Takeru Kinoshita, Hideo Kobayashi, Youichi Usui, Ryo Ohkubo, Shinichi Ishibashi, and Osamu Nagarekawa "Process development of 6-in EUV mask with TaBN absorber", Proc. SPIE 4754, Photomask and Next-Generation Lithography Mask Technology IX, (1 August 2002); https://doi.org/10.1117/12.477007

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

;

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE