You have requested a machine translation of selected content from our databases. This functionality is provided solely for your convenience and is in no way intended to replace human translation. Neither SPIE nor the owners and publishers of the content make, and they explicitly disclaim, any express or implied representations or warranties of any kind, including, without limitation, representations and warranties as to the functionality of the translation feature or the accuracy or completeness of the translations.
Translations are not retained in our system. Your use of this feature and the translations is subject to all use restrictions contained in the Terms and Conditions of Use of the SPIE website.
20 July 2004Damage analysis of CF/AF hybrid fabric reinforced plastic laminated composites with scanned image microscopy
The article presents an experimental study that has been conducted to evaluate the impact loading damage within hybrid fabric laminates-carbon and Aramid fibers. The experiments have been undertaken on a series of interply hybrid specimens with different preprags stacking sequences. Impact damage was created using an air-gun like impact device propelling spherical steel balls with diameters of 5.0mm and 10.0mm and having velocities of 113m/s and 40m/s respectively. The resulting specimen surface and internal damage (e.g., micro-cracking and debonding) was visualized nondestructively by a scanning acoustic microscope (SAM) while further interrogation of specific internal damage was visualized using a scanning electron microscope (SEM) on cross-sectioned panels.
Chiaki Miyasaka,Hideaki Kasano, andPeter J. Shull
"Damage analysis of CF/AF hybrid fabric reinforced plastic laminated composites with scanned image microscopy", Proc. SPIE 5393, Nondestructive Evaluation and Health Monitoring of Aerospace Materials and Composites III, (20 July 2004); https://doi.org/10.1117/12.548594
The alert did not successfully save. Please try again later.
Chiaki Miyasaka, Hideaki Kasano, Peter J. Shull, "Damage analysis of CF/AF hybrid fabric reinforced plastic laminated composites with scanned image microscopy," Proc. SPIE 5393, Nondestructive Evaluation and Health Monitoring of Aerospace Materials and Composites III, (20 July 2004); https://doi.org/10.1117/12.548594