Sulfuric acid treatment of indium tin oxide for application of organic light-emitting diodes

Wei-zhi Li; Xing-qiao Ji; Zhi-you Zhong; Tao Wang; Ya-dong Jiang

doi:10.1117/12.667366

26 January 2006 Sulfuric acid treatment of indium tin oxide for application of organic light-emitting diodes

Wei-zhi Li, Xing-qiao Ji, Zhi-you Zhong, Tao Wang, Ya-dong Jiang

Proceedings Volume 6030, ICO20: Display Devices and Systems; 60300A (2006) https://doi.org/10.1117/12.667366
Event: ICO20:Optical Devices and Instruments, 2005, Changchun, China

Abstract

In this paper, indium tin oxide (ITO) substrates were treated by ethanol, sulfuric acid (98%) and oxygen plasma respectively, based on which organic light-emitting diodes (OLEDs) with the same double-layer structure: ITO/N,N'-bis-(1-naphyl)-N,N'-diphenyl-1,1'- biphenyl-4,4'-diamine(NPB)/tris-(8-hydroxyquinoline) aluminum(Alq3)/ Mg:Ag/Al were fabricated. The morphology and compositions of differently treated ITO films were analyzed by atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). AFM results showed that all these treatments didn't change much the average roughness of ITO films, while ethanol has little influence on the large "peak-valley" (P-V) distance of ITO film; ITO film treated by sulfuric acid has suitable surface morphology with low P-V distance, low average roughness and small particle radius. XPS analysis proved that ethanol has the weakest ability to remove carbon contamination on the surface of ITO film which resulted in unevenly distributed current and high barriers for hole injection; sulfuric-acid-treated ITO film has the least contamination of carbon and higher concentration of oxygen vacancies, both of which are helpful for the improvement of devices. In the condition of room temperature and atmosphere and without encapsulation, measurements of the current-voltage, brightness-voltage and lifetime characteristics of these devices were conducted and showed good agreement with what expected from the results of AFM and XPS analysis: the ethanol-treated ITO provides very unstable performance with low efficiency for the device based on it, while the device based on sulfuric-acid-treated ITO anode had even better performance at higher driven voltage (>7V) comparing with the device based on oxygen-plasma-treated ITO substrate and had the highest current-luminance efficiency (3.2 cd/A) and the longest lifetime (2 hours).

Citation Download Citation

Wei-zhi Li, Xing-qiao Ji, Zhi-you Zhong, Tao Wang, and Ya-dong Jiang "Sulfuric acid treatment of indium tin oxide for application of organic light-emitting diodes", Proc. SPIE 6030, ICO20: Display Devices and Systems, 60300A (26 January 2006); https://doi.org/10.1117/12.667366

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available