1 August 2007 Absorption and photoluminescence of Ga0.017Ge0.25As0.083S0.65 glasses doped with rare-earth ions
Author Affiliations +
Proceedings Volume 6785, ROMOPTO 2006: Eighth Conference on Optics; 678519 (2007) https://doi.org/10.1117/12.757919
Event: ROMOPTO 2006: Eighth Conference on Optics, 2006, Sibiu, Romania
Abstract
The visible luminescence from Pr3+, Dy3+, Nd3+, Sm3+ and codoped with Ho3+ and Dy3+ ions embedded in Ga0.017Ge0.25As0.083S0.65 glass hosts at room temperature and at T=10 K is reported, when pumping with an Ar+-ion laser at λ=488 nm. Fluorescence emissions at 1.3 μm was observed for Dy3+ and both at 1.3 and at 1.5 μm for Pr3+ doped glasses with wavelength pumping at 950 nm. Energy transfer from Ho3+:5F3 level to Dy3+:4F9/2 level increase the visible emission efficiency at 650 nm in the codoped glasses. The investigated Ga0.017Ge0.25As0.083S0.65 glasses doped with Pr3+ are promising amplifier materials for 1.3 and 1.5 μm fiber optic telecommunication windows.
© (2007) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
M. S. Iovu, A. M. Andriesh, E. V. Lupan, V. I. Ciornea, and N. N. Syrbu "Absorption and photoluminescence of Ga0.017Ge0.25As0.083S0.65 glasses doped with rare-earth ions", Proc. SPIE 6785, ROMOPTO 2006: Eighth Conference on Optics, 678519 (1 August 2007); https://doi.org/10.1117/12.757919
PROCEEDINGS
6 PAGES


SHARE
Advertisement
Advertisement
Back to Top