Continued advancement of laser damage resistant optically functional microstructures

Douglas S. Hobbs; Bruce D. MacLeod; Ernest Sabatino III

doi:10.1117/12.976909

4 December 2012 Continued advancement of laser damage resistant optically functional microstructures

Douglas S. Hobbs, Bruce D. MacLeod, Ernest Sabatino III

Author Affiliations +

Proceedings Volume 8530, Laser-Induced Damage in Optical Materials: 2012; 85300O (2012) https://doi.org/10.1117/12.976909
Event: SPIE Laser Damage, 2012, Boulder, Colorado, United States

Abstract

Micro- and nano-structured optically functional surface textures continue to exhibit higher performance and longer term survivability than thin-film coatings for an increasing number of materials used within high energy laser (HEL) systems. Anti-reflection (AR) microstructures (ARMs) produce a graded refractive index yielding high transmission over wide spectral ranges along with a chemical, mechanical and laser damage resistance inherited from the bulk optic material. In this study, ARMs were fabricated in the relevant HEL materials sapphire, neodymium-doped YAG, fused silica, BK7 glass, and the magnesium aluminate known as SPINEL. Standardized pulsed laser induced damage threshold (LiDT) measurements were made using commercial testing services to directly compare the damage resistance of ARMs-treated optics to uncoated and thin-film-AR-coated (TFARC) optics at wavelengths of 532nm, 694nm, 800nm, 1064nm, and 1538nm. As found with prior work, the LiDT of ARMs etched in fused silica was typically in the range of 35 J/cm² at a wavelength of 1064nm and a pulse width of 10ns, a level that is comparable to uncoated samples and 3.5 times greater than the level specified by six prominent TFARC providers. The Army Research Laboratory measured the pulsed LiDT at 532nm (10ns) of ARMs in fused silica to be up to 5 times the level of the ion beam sputtered TFARC previously employed in their HEL system, and 2 times higher than a low performance single layer MgF₂ TFARC. This result was repeated and expanded using a commercial LiDT testing service for ARMs in two types of fused silica and for Schott N-BK7 glass. An average damage threshold of 26.5 J/cm² was recorded for the ARMs-treated glass materials, a level 4 times higher than the commercial IBS TFARCs tested.

Citation Download Citation

Douglas S. Hobbs, Bruce D. MacLeod, and Ernest Sabatino III "Continued advancement of laser damage resistant optically functional microstructures", Proc. SPIE 8530, Laser-Induced Damage in Optical Materials: 2012, 85300O (4 December 2012); https://doi.org/10.1117/12.976909

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

;

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE