19 April 2013 Smart multifunctional cement mortar containing graphite nanoplatelet
Author Affiliations +
Abstract
The piezoresistivity-based strain sensing ability of cementitious composites containing graphite nanoplatelet (GNP) is investigated in this paper. GNP offers the advantages of ease of processing, excellent mechanical and electrical properties at a very low cost compared to carbon nanotubes and carbon nano-fibers. Cement mortar with 0%, 1.2%, 2.4%, 3.6% and 4.8% of GNP (by volume of composite) were cast. The electrical resistance of the specimens was measured by both the two- and four-probe methods using direct current (DC). The effect of polarization was characterized and the percolation threshold was experimentally found to be between 2.4% and 3.6% of GNP based on both accelerated and normal drying specimens. The assumption of Ohmic material was tested with varying current and found to be valid for current < 0.01mA and 0.5mA for four- and two-probe methods respectively. The piezoresistive effect was demonstrated by comparing the gage factors of mortars with GNP vs plain mortar under cyclic loading in compression at 3 strain levels. At low strains, the high gage factor is believed to stem from both the effect of the imperfect interfaces around the GNP and the piezoresistivity of the GNP; at higher strains, the gage factor is likely to be attributed to the piezoresistivity of the GNP and it is still 1-2 orders of magnitude larger than the gage factor arising from geometric changes.
© (2013) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Hongjian Du, Ser Tong Quek, and Sze Dai Pang "Smart multifunctional cement mortar containing graphite nanoplatelet", Proc. SPIE 8692, Sensors and Smart Structures Technologies for Civil, Mechanical, and Aerospace Systems 2013, 869238 (19 April 2013); https://doi.org/10.1117/12.2009005
PROCEEDINGS
10 PAGES


SHARE
Advertisement
Advertisement
Back to Top