20 May 2013 Observation of morphology of V2O5 nanorods grown by electron beam irradiation using confocal microscope
Author Affiliations +
Proceedings Volume 8879, Nano-Bio Sensing, Imaging, and Spectroscopy; 88790M (2013) https://doi.org/10.1117/12.2018716
Event: Nano-Bio Sensing, Imaging and Spectroscopy, 2013, Jeju, Korea, Republic of
Abstract
In order to confirm an applying capability of the CLSM, the V2O5 nanorods grown by the electron beam irradiation and the thermal oxidation methods were used as nanostructures, and the CLSM was composed in our laboratory. The theoretical resolution of the hand-made CLSM was found to be a 150 nm and evaluated by observing image of an USAF target.The morphologies of the grown V2O5 nanorods grown were observed by the CLSM, and the morphologies were compared with those obtained by the SEM. From the comparison with the result by the SEM, the magnification and the resolution of the CLSM were estimated to be approximately 2000 and 500 nm, respectively. On the basis of this result, it was considered that the CLSM can be used to measure the morphology of the nanostructures with a submicro-scale.
© (2013) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Manil Kang, Donghyuk Hong, Taesung Kim, Minwoo Chu, and Sok Won Kim "Observation of morphology of V2O5 nanorods grown by electron beam irradiation using confocal microscope", Proc. SPIE 8879, Nano-Bio Sensing, Imaging, and Spectroscopy, 88790M (20 May 2013); https://doi.org/10.1117/12.2018716
PROCEEDINGS
7 PAGES


SHARE
Advertisement
Advertisement
Back to Top