You have requested a machine translation of selected content from our databases. This functionality is provided solely for your convenience and is in no way intended to replace human translation. Neither SPIE nor the owners and publishers of the content make, and they explicitly disclaim, any express or implied representations or warranties of any kind, including, without limitation, representations and warranties as to the functionality of the translation feature or the accuracy or completeness of the translations.
Translations are not retained in our system. Your use of this feature and the translations is subject to all use restrictions contained in the Terms and Conditions of Use of the SPIE website.
1 May 2014Photoelectrical properties of indandione fragment containing azobenzene compounds
Organic materials are becoming more popular due to their potential application in electronics. Low molecular weight materials possible produce from solution are in special consideration. It gives the possibility to avoid both thermal evaporation in vacuum, and use of polymers in thin film preparation process. Indandione fragment containing azobenzene compounds are one of such materials. These compounds are good candidates for use in design of novel molecular electronic devices due to their possibility to form amorphous structure from solution thus allowing developing flexible, small size systems with low production costs. In this work three indandione fragment containing azobenzene compounds were investigated. Difference between these compounds is bulky groups which assist formation of amorphous thin film. Absorption spectra of the investigated compounds are similar to P3HT but with higher absorption coefficient. Molecule ionization and electron affinity levels of these compounds are around -5.45eV and -3.80eV, respectively. Combining PCBM with investigated compounds could lead to difference between electron affinity levels maximum of 0.15eV. It is several times less compared to ~1eV for P3HT:PCBM system. Higher difference between the donor ionization level and the acceptor affinity level could also be obtained which should lead to the higher open circuit voltage.