1 June 2015 Luminescence yield in Al and Tb3+delta-doped oxide thin films fabricated by electron beam evaporation
Author Affiliations +
Electron beam evaporation was employed in order to fabricate Al- and Tb-codoped Si oxide multilayers via the delta-doping approach. This methodology permits the control of the rare-earth (RE) separation along the growth direction with nanometric resolution. To investigate the control of the RE separation in the growth direction, different SiO2 thicknesses were studied. After deposition, the samples were submitted to different annealing processes for 1 h in N2, at temperatures ranging from 700 to 1100 °C. Photoluminescence experiments reveal narrow emissions ascribed to Tb3+ ions in all samples, with an intensity variation depending on the oxide thickness and annealing temperature. In addition, the incorporation of Al under different spatial configurations produced an enhancement of more than one order of magnitude in the photoluminescence intensity, in respect to the best sample without Al. Finally, time-resolved measurements were carried out in order to determine the 5D47F5 transition dynamics, obtaining a decay time of ~1.6 ms ascribed to the Tb3+ ions.
© (2015) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
O. Blázquez, J. M. Ramírez, J. López-Vidrier, Y. Berencén, S. Hernández, P. Sanchis, and B. Garrido "Luminescence yield in Al and Tb3+delta-doped oxide thin films fabricated by electron beam evaporation", Proc. SPIE 9520, Integrated Photonics: Materials, Devices, and Applications III, 95200K (1 June 2015);

Back to Top