12 May 2020 Liquid crystal integrated metalens with tunable chromatic aberration
Author Affiliations +
Abstract

Overcoming chromatic aberrations is a vital concern in imaging systems in order to facilitate full-color and hyperspectral imaging. By contrast, large dispersion holds opportunities for spectroscopy and tomography. Combining both functions into a single component will significantly enhance its versatility. A strategy is proposed to delicately integrate two lenses with a static resonant phase and a switchable geometric phase separately. The former is a metasurface lens with a linear phase dispersion. The latter is composed of liquid crystals (LCs) with space-variant orientations with a phase profile that is frequency independent. By this means, a broadband achromatic focusing from 0.9 to 1.4 THz is revealed. When a saturated bias is applied on LCs, the geometric phase modulation vanishes, leaving only the resonant phase of the metalens. Correspondingly, the device changes from achromatic to dispersive. Furthermore, a metadeflector with tunable dispersion is demonstrated to verify the universality of the proposed method. Our work may pave a way toward active metaoptics, promoting various imaging applications.

1.

Introduction

The development of nanostructured metasurfaces has offered unprecedented capabilities for the advance of planar optics.13 Among various metadevices, the metalens attracts widespread attention due to practical applications in imaging and spectroscopy.47 Recently, metalenses composed of specific subwavelength metallic or dielectric resonator arrays have been developed for multifunctional wavefront manipulations,812 replacing the traditional refractive lenses made of precisely polished crystals or polymers. These metalenses embrace the trend of miniaturization and integration of photonic systems. Nevertheless, their functions remain static once they are fabricated. Therefore, many researchers are focusing on realizing active metalenses via introducing MEMS,13 semiconductors,14,15 phase-change materials,1618 graphene,19 and liquid crystals (LCs)20,21 with external field induced responsivity. The majority of them possess either switchable bifocal properties or a limited tuning range. Until now, dynamic functions, especially continuously variable focal length or tunable chromatic aberration, have remained formidable challenges.

In many cases, metalenses suffer from large chromatic aberrations, which severely degrade the resolution of full-color and hyperspectral imaging. Compared with optical or near-IR metalenses, the chromatic aberration of their terahertz (THz) counterparts is more significant, due to the broadband of THz spectrum.22 It induces a frequency-varying focal length and drastically degrades the resolution of spectral-resolved THz imaging.23,24 To solve this problem, mechanical scanning along the optical path is required to capture images at different frequencies,25 which makes the detection and analysis complicated and time-consuming. More recently, inspired by achromatic metalens designs in the visible and near-IR range,2630 broadband achromatic focusing has been realized in the THz regime via dispersive phase compensation from C-shape silicon micropillar arrays.31 By contrast, for spectrographic and tomographic applications,32,33 large chromatism is favored to separate focal spots of different frequencies spatially without crosstalk.34,35 If dynamic alternation between the achromatic and dispersive focusing properties can be achieved using a single metalens, it would greatly promote the practical applications of spectroscopy and imaging systems.

In this paper, we propose a transmission-type THz metalens with tunable chromatic aberration. The metalens integrates a dielectric metasurface with photopatterned LCs and exhibits a broadband achromatism. When a saturated voltage is applied on the transparent graphene electrodes, a dispersive focusing function is revealed. The performance of the metalens is characterized and consistent with numerical simulations. Further, THz imaging performed with this metalens also verifies its tunable functions. This approach may open an avenue for designing active metalenses in versatile applications.

2.

Results

2.1.

Principle and Design

Figures 1(a) and 1(b) schematically illustrate the tunable functions of the proposed metalens. The achromatism is accomplished by delicately designing the integrated resonant phase (φR) and geometric phase (φG). Geometries of silicon pillar meta-units36,37 vary from the center to the edge, enabling a frequency-dependent lens phase profile. The space-variant alignments of LCs38 perform a frequency-independent φG modulation. Without the applied voltage, it works as a broadband achromatic lens, where light within the designed spectrum deflects to the same focal spot. When applying a saturated bias on the graphene electrodes39 covered on both sides of the LC layer, LCs are reoriented perpendicularly to the substrates. Thus the φG modulation vanishes and only the φR of the metaunits works. Correspondingly, the device turns into a chromatic lens with an anomalous dispersion, i.e., the focal length decreases when the frequency increases.

Fig. 1

Schematic function tunability and designs of the metalens. (a) The broadband achromatic focusing state without bias. (b) The dispersive focusing state with a saturated bias. The superstrate depicts the dielectric metasurface while the blue ellipsoids between the superstrate and substrate denote LCs. (c) Dependencies of φR (red curve) and PCR of a silicon pillar metaunit on f. Inset shows the dimensions of the unit. Dependency of φR on l and w at (d) 0.9 and (e) 1.4 THz, respectively. (f) Dispersion ratio of the silicon pillar as a function of l and w under LCP incidence. Dependency of PCR on l and w at (g) 0.9 and (h) 1.4 THz. The region circled by the black dashed line indicates a PCR over 12% from 0.9 to 1.4 THz. (i) Designed l and w of the silicon pillars along r from the center to the edge. (j) φA and φR at 0.9 (blue solid and dashed curves) and 1.4 THz (red solid and dashed curves) and residual φG. (k) Target φG and corresponding LC director distributions are labeled by the orange lines.

AP_2_3_036002_f001.png

The generalized phase profile of an achromatic lens is expressed as

Eq. (1)

φA(f,r)=2πfc(F2+r2F)+Δφ(f),
where f denotes the working frequency, c is the light velocity in vacuum, F is the focal length, and r is the radius of an arbitrary point on the lens. The additional phase Δφ is only related to f, which is introduced for dispersion compensation (see Fig. S1 in the Supplementary Material). If a linear function is established between Δφ and f, namely, Δφ=kf+d (k and d are constants), φA can be transformed to

Eq. (2)

φA(f,r)=[k2πc(F2+r2F)]f+d.

From Eq. (2), at a certain r, the required φA shows a linear relationship with f. Such a linear dispersion can be satisfied by high-order waveguide resonances excited inside the dielectric pillars with a high aspect ratio and large dielectric constant40 (Fig. S2 in the Supplementary Material). Apart from the former dispersion item achieved by the φR, the constant d is frequency-independent and can be accomplished through introducing the φG, namely the Pancharatnam–Berry phase.41 It originates from the photonic spin–orbit interaction and can be created via controlling the geometric orientation angle θ of anisotropic media, e.g., LCs and metaresonators.42,43 Theoretically, φG is twice θ and conjugated at left-handed and right-handed circular polarization (LCP/RCP) incidences.

As a proof-of-concept demonstration, an achromatic lens with F=15.0  mm from 0.9 to 1.4 THz was designed. In Fig. 1(c), φR and the polarization conversion ratio (PCR, determining the efficiency of the metalens) of a silicon pillar metaunit with l=50  μm, w=36  μm, h=200  μm, and p=60  μm are simulated and presented as an example. To simplify the simulation, we fix h and p and then vary l and w in the range of 10 to 50  μm to achieve a library of dispersion ratios (defined as dφR/df), as shown in Fig. 1(f). dφR/df increases with l and w separately. The abnormal values along the diagonal are due to the near zero PCR when l=w. φR and PCR are also related to l and w; the dependencies of φR on them at 0.9 and 1.4 THz are shown in Figs. 1(d) and 1(e), respectively. The π phase difference of φR on mirrored sides of l=w is due to the additional φG induced by a 90-deg rotation of the metaunit. To achieve the desired achromatic property, the geometry of metaunits at different r should be deliberately selected. In addition to the dispersion factor dφR/df, φR should be further considered to maintain a lens profile. Figures 1(g) and 1(h) exhibit the dependency of PCR on l and w. For optimized efficiency, only parameters in the black-dashed region are used. Due to the limited range of dφR/df (41.8  rad/THz at l=48  μm, w=10  μm to 49.5  rad/THz at l=50  μm, w=44  μm), r of the metalens is limited to 3240  μm, i.e., 54 units. According to this design, the l and w of the silicon pillars along r are presented in Fig. 1(i). It is observed that l remains nearly unchanged around 50  μm, whereas w gradually decreases from the center to the edge. Figure 1(j) plots the φR and φA at 0.9 and 1.4 THz. The f-independent and r-dependent gap between φA and φR can be compensated for by φG. The corresponding φG profile [Fig. 1(k)] can be precisely accomplished by locally varying the LC directors, as shown schematically in the overlay.

2.2.

Focusing Performance Characterizations

Figures 2(a)2(d) present the SEM images of the fabricated metasurface. Figure 2(a) shows a part of the metasurface from the top view. The silicon pillars close to the center and the edge are labeled by orange and blue dashed squares, respectively. Corresponding zoomed-in images in Figs. 2(b) and 2(c) show well-defined microstructures, which faithfully follow the design [Fig. 1(i)]. The cross-section image of the metasurface is exhibited in Fig. 2(d). Some broken pillars resulting from the damage caused in the cutting process are observed. Due to the different etching speeds for the varying aspect ratio in the fabrication, pillars near the edge [the right side in Fig. 2(d)] are higher than those near the center (left side) (detailed in Fig. S3 in the Supplementary Material). The photopatterned LCs are observed under the microscope with crossed polarizers. The optical image of the whole LC region is displayed in Fig. 2(e), in which the gray scales are consistent with the φG shown in Fig. 1(k). As the φG is pixelated with the same periodicity of 60  μm as that of silicon metaunits, gray scale pixels are vividly revealed in the zoomed-in image in Fig. 2(f).

Fig. 2

Characterization of the metalens. (a) SEM image of the metasurface (top view). Scale bar: 300  μm. Zoomed-in images of the silicon pillars labeled by the (b) orange and (c) blue squares in (a), respectively. (d) Cross-section image of the metasurface. Scale bars in (b)–(d): 100  μm. (e) Optical image of the LC layer under crossed polarizers. (f) A zoomed-in image labeled by the orange square in (e). Scale bars in (e) and (f) are 1 mm and 500  μm, respectively.

AP_2_3_036002_f002.png

We use a scanning near-field THz microscope (SNTM) to characterize the performance of the LC integrated metalens. The normalized intensity distributions from 0.9 to 1.4 THz with an interval of 0.1 THz are simulated and measured at the bias OFF and saturated states, respectively (Fig. S4 in the Supplementary Material). Figure 3(a) selectively reveals the simulated THz fields at 0.9, 1.1, and 1.4 THz in the xz plane at bias OFF. The measured F remains unchanged around 12.0 mm within the designed spectrum [Fig. 3(b)], which is consistent with the simulation. Little distortions are observed at 0.9 and 1.1 THz, which is mainly attributed to the slightly tilt incidence of the THz beam. The THz fields in the xy plane (z=12.0  mm) and the corresponding transverse intensity profiles are also exhibited, verifying the perfect achromatic focusing property. It is noticed that the F is slightly smaller than the design as a result of the gradual etching depth deviation (see Sec. S2 in the Supplementary Material). This deviation is also considered in the simulation. After a square-wave alternating voltage (75 Vrms, 1 kHz) is applied, both the simulated and measured results [Figs. 3(c) and 3(d)] show a significant F dispersion among different f from 0.9 to 1.4 THz. It is noticed that, as the φG is spin-dependent, the metalens only works at the LCP THz incidence when the bias is OFF, whereas it works at both LCP/RCP incidences when the bias is saturated due to the spin-independent φR. LCs can be electrically tuned to match the half-wave conditions at different f to generate a complete geometric phase modulation, contributing to the achromatic case. Mismatch from the half-wave condition causes the residual unmodulated wave, contributing to the dispersive case. Thus via tuning the applied voltage, the required circular polarization incidence of the metasurface is satisfied.

Fig. 3

Focusing performance of the metalens. (a) Simulated THz fields in the xz plane and (b) measured THz fields in the xz and xy plane (z=12.0  mm) at 0.9, 1.1, and 1.4 THz, respectively, when no bias is applied. (c) Simulated and (d) measured THz fields in the xz and xy plane (z=13.0  mm) of the same sample with a saturated bias. Dashed lines in (a)–(d) label the corresponding focal planes. White curves in (b) and (d) depict the transverse intensity distributions at z=12.0 and 13.0 mm, respectively. (e) Simulated and measured F, (f) FWHM at z=12.0 and 13.0 mm in (b) and (d), separately, and (g) measured device efficiency, as a function of f. The black dashed line in (f) depicts the diffraction-limited FWHM.

AP_2_3_036002_f003.png

The dependencies of F on f at both the bias OFF and saturated states are quantified in Fig. 3(e). The results satisfactorily verify the function tunability from achromatic to dispersive. Full-widths at half-maximum (FWHMs) of the intensity profile at different f are shown in Fig. 3(f). The values at the achromatic state [z=12.0  mm in Fig. 3(b)] are very close to the ideal diffraction limit (λ/2 NA), whereas distinct deviations are observed at the dispersive state [z=13.0  mm in Fig. 3(d)] due to the defocusing at lower f. Figure 3(g) exhibits the measured efficiency, which is defined as the ratio of THz intensity at the focal plane to the incident LCP THz power. The average efficiency of the dispersive case (33.9%) is higher than that of the achromatic one (26.1%), which is attributed to the additional PCR loss caused by LCs. The total efficiency is determined by several factors: the PCR of the metaunits and LCs, the absorption and scattering of all transmitted layers, and the imperfect fabrication of the sample. These issues can be addressed by further optimizing the metaunit geometry and the LC layer thickness and introducing low-loss substrates (detailed analysis in Sec. S4 in the Supplementary Material).

2.3.

Dynamic THz Imaging

The imaging performance of the metalens is further characterized, utilizing the setup schematically illustrated in Fig. 4(a). After generation with a photoconductive antenna,44 the linearly polarized THz wave is converted to LCP with a quarter-wave plate. The THz beam transmits the object and subsequently the metalens; then it is scanned by the probe. The object is a “smiling face” with a diffraction-limited resolution. The object distance u and image distance v are designed as both 24.0 mm to obtain an image with an equal size of the object when F=12.0  mm. The intensity and phase distributions from 0.9 to 1.4 THz with an interval of 0.1 THz are measured at the bias OFF and saturated states (Fig. S5 in the Supplementary Material). At the bias OFF state, a multispectral imaging is realized, where the smiling face can be distinctly observed at any f within the spectrum. When the bias is saturated, the imaging quality becomes poorer at lower f due to the deviation of F from 12.0 mm. Figures 4(b)4(e) show the corresponding intensity and phase distributions at 0.9 and 1.4 THz. The transverse intensities across two “eyes” and the “mouth” are clearly recognized in Figs. 4(b), 4(c), and 4(e), indicating a satisfactory imaging quality. The smiling face is distinguishable in corresponding phase distributions as well. However, the imaging effect is poor in Fig. 4(d) due to the remarkable defocusing. The imaging quality can be further enhanced via enlarging the NA of the metalens. A simple and effective method is increasing the h of the silicon pillars while maintaining the other parameters (see Fig. S6 in the Supplementary Material).

Fig. 4

Broadband THz imaging. (a) Schematic of the SNTM setup. The inset exhibits the micrograph of the object “smiling face,” where the scale bar indicates 1 mm. Measured intensity and phase distributions at (b) 0.9 and (c) 1.4 THz without bias. The white and orange curves depict the intensity profiles along the white and orange dashed lines, respectively. The outline of the object “smiling face” is labeled by black dashed lines in the phase diagrams. Measured intensity and phase distributions at (d) 0.9 and (e) 1.4 THz with a saturated bias.

AP_2_3_036002_f004.png

2.4.

Active Metadeflector

The proposed strategy can be rationally extended to the design of various active metadevices beyond the metalens. We numerically demonstrate a beam deflector with tunable dispersion in Fig. S8. It is composed of silicon metaunits with geometries varying along the x axis and LCs with gradient orientation distributions. The combination of φR and φG contributes to a fixed deflection angle of 17 deg from 0.9 to 1.4 THz. When the LCs are reoriented along the z axis, the deflection becomes dispersive (details in Sec. S5 in the Supplementary Material).

3.

Experimental Section

3.1.

Sample Fabrication

The fabrication process of the LC integrated metalens is schematically illustrated in Fig. S9 in the Supplementary Material. The metasurface is fabricated via the standard photolithography process followed by a reactive ion etching on a 500-μm-thick intrinsic silicon wafer. Then the residual photoresist is lifted off. Both the metasurface and silica substrate are ultrasonically cleaned and O-plasma treated for 10 min. Then they are transferred with few-layer graphene from copper foil (Six Carbon Technology, China). After that, they are spin-coated at 3000 rpm for 30 s with photoalignment agent SD145,46 (Dai-Nippon Ink and Chemicals, Japan) and baked at 100°C for 10 min to remove the solvent. Then the metasurface and silica substrate are assembled with a 250-μm-thick Mylar spacer to form a cell. A digital micromirror device-based dynamic microlithography47,48 is employed to perform the photopatterning process. Then the LC NJU-LDn-449 with an average birefringence over 0.3 within the designed spectrum is infiltrated at 180°C and self-assembled to the desired orientations. The imaging object “smiling face” is fabricated via photolithography followed by an electron beam evaporation to deposit Au on the silicon substrate.

3.2.

Numerical Simulation

The parameter sweep and selection of silicon pillar metaunits and the focusing performance simulation of the metalens are carried out using a commercial software (Lumerical FDTD Solutions). Due to the geometric symmetry of the lens, the model along the radius is established to simplify the simulation. The LC layer is divided into small domains. Each domain is set as a 60  μm×60  μm×250  μm (x×y×z) cuboid. The LC is a diagonal dielectric material with no=1.56 (diagonal elements xx and yy) and ne=1.88 (diagonal element zz). The LC director distributions are set by an LC orientation module. An LCP plane wave with a spectrum range from 0.9 to 1.4 THz is incident along the z axis.

3.3.

Characterizations

An SNTM setup (Terahertz Photonics Co., Ltd., China), which is based on the photoconductive THz generation and detection, is utilized to characterize the performance of the metalens. In the setup, a scanning tip fixed on a motorized stage [Fig. 4(a)] is utilized to record the Ex field in the xy plane with a step size of 0.25 mm. The sample moves along the z axis with a step size of 1 mm to capture the Ex field in the xz plane. Then an interpolation algorithm is adopted to obtain the measured THz fields.

4.

Conclusion

We developed an LC integrated metalens with tunable chromatic aberration. The geometric phase of photopatterned LCs and the resonant phase of the dielectric metasurface together contribute to the broadband achromatic focusing. While applying a saturated voltage to LCs, the geometric phase modulation vanishes and the metalens exhibits a dispersive focusing. Simulated and experimental results of such active functions reveal a good consistency. Moreover, multispectral THz imaging using this metalens is demonstrated, indicating great potential in advanced THz spectroscopy and imaging apparatuses. This strategy can also be extended to other electromagnetic spectra, e.g., the visible and near-IR, where lenses with integrated tunable functions are highly desired for full-color imaging and tomography. A metadeflector with tunable dispersion is further demonstrated, which verifies the versatility of the proposed solution for various metadevices toward active metaoptics.

Acknowledgments

The authors gratefully acknowledge the support of the National Key Research and Development Program of China (No. 2017YFA0303700), the National Natural Science Foundation of China (NSFC) (No. 61922038), the Distinguished Young Scholars Fund of Jiangsu Province (No. BK20180004), and the Fundamental Research Funds for the Central Universities (No. 021014380118). W. H. gratefully acknowledges the support of the Tang Scholar Program. The authors declare no conflicts of interest.

References

1. 

A. V. Kildishev, A. Boltasseva and V. M. Shalaev, “Planar photonics with metasurfaces,” Science, 339 1232009 (2013). https://doi.org/10.1126/science.1232009 SCIEAS 0036-8075 Google Scholar

2. 

N. Yu and F. Capasso, “Flat optics with designer metasurfaces,” Nat. Mater., 13 139 (2014). https://doi.org/10.1038/nmat3839 NMAACR 1476-1122 Google Scholar

3. 

P. Genevet et al., “Recent advances in planar optics: from plasmonic to dielectric metasurfaces,” Optica, 4 (1), 139 –152 (2017). https://doi.org/10.1364/OPTICA.4.000139 Google Scholar

4. 

M. Khorasaninejad et al., “Metalenses at visible wavelengths: diffraction-limited focusing and subwavelength resolution imaging,” Science, 352 1190 –1194 (2016). https://doi.org/10.1126/science.aaf6644 SCIEAS 0036-8075 Google Scholar

5. 

P. Lalanne and P. Chavel, “Metalenses at visible wavelengths: past, present, perspectives,” Laser Photonics Rev., 11 (3), 1600295 (2017). https://doi.org/10.1002/lpor.201600295 Google Scholar

6. 

M. Khorasaninejad and F. Capasso, “Metalenses: versatile multifunctional photonic components,” Science, 358 eaam8100 (2017). https://doi.org/10.1126/science.aam8100 SCIEAS 0036-8075 Google Scholar

7. 

M. L. Tseng et al., “Metalenses: advances and applications,” Adv. Opt. Mater., 6 (18), 1800554 (2018). https://doi.org/10.1002/adom.201800554 2195-1071 Google Scholar

8. 

M. Khorasaninejad et al., “Polarization-insensitive metalenses at visible wavelengths,” Nano Lett., 16 (11), 7229 –7234 (2016). https://doi.org/10.1021/acs.nanolett.6b03626 NALEFD 1530-6984 Google Scholar

9. 

Q. Yang et al., “Broadband and robust metalens with nonlinear phase profiles for efficient terahertz wave control,” Adv. Opt. Mater., 5 (10), 1601084 (2017). https://doi.org/10.1002/adom.201601084 2195-1071 Google Scholar

10. 

S. Shrestha et al., “Broadband achromatic dielectric metalenses,” Light Sci. Appl., 7 8 (2018). https://doi.org/10.1038/s41377-018-0078-x Google Scholar

11. 

W. T. Chen et al., “A broadband achromatic polarization-insensitive metalens consisting of anisotropic nanostructures,” Nat. Commun., 10 355 (2019). https://doi.org/10.1038/s41467-019-08305-y NCAOBW 2041-1723 Google Scholar

12. 

V. C. Su et al., “Advances in optical metasurfaces: fabrication and applications,” Opt. Express, 26 (10), 13148 –13182 (2018). https://doi.org/10.1364/OE.26.013148 OPEXFF 1094-4087 Google Scholar

13. 

E. Arbabi et al., “MEMS-tunable dielectric metasurface lens,” Nat. Commun., 9 (1), 812 (2018). https://doi.org/10.1038/s41467-018-03155-6 NCAOBW 2041-1723 Google Scholar

14. 

K. Chen et al., “A reconfigurable active Huygens’ metalens,” Adv. Mater., 29 (17), 1606422 (2017). https://doi.org/10.1002/adma.201606422 ADVMEW 0935-9648 Google Scholar

15. 

A. Afridi et al., “Electrically driven varifocal silicon metalens,” ACS Photonics, 5 (11), 4497 –4503 (2018). https://doi.org/10.1021/acsphotonics.8b00948 Google Scholar

16. 

X. Yin et al., “Beam switching and bifocal zoom lensing using active plasmonic metasurfaces,” Light Sci. Appl., 6 (7), e17016 (2017). https://doi.org/10.1038/lsa.2017.16 Google Scholar

17. 

Q. Wang et al., “Optically reconfigurable metasurfaces and photonic devices based on phase change materials,” Nat. Photonics, 10 (1), 60 –65 (2016). https://doi.org/10.1038/nphoton.2015.247 NPAHBY 1749-4885 Google Scholar

18. 

A. Karvounis et al., “All-dielectric phase-change reconfigurable metasurface,” Appl. Phys. Lett., 109 (5), 051103 (2016). https://doi.org/10.1063/1.4959272 APPLAB 0003-6951 Google Scholar

19. 

W. Liu et al., “Graphene-enabled electrically controlled terahertz meta-lens,” Photonics Res., 6 (7), 703 –708 (2018). https://doi.org/10.1364/PRJ.6.000703 Google Scholar

20. 

C. Y. Fan et al., “Electrically modulated varifocal metalens combined with twisted nematic liquid crystals,” Opt. Express, 28 (7), 10609 –10617 (2020). https://doi.org/10.1364/OE.386563 OPEXFF 1094-4087 Google Scholar

21. 

J. Beeckman et al., “Multi-electrode tunable liquid crystal lenses with one lithography step,” Opt. Lett., 43 (2), 271 –274 (2018). https://doi.org/10.1364/OL.43.000271 OPLEDP 0146-9592 Google Scholar

22. 

B. Ferguson and X. C. Zhang, “Materials for terahertz science and technology,” Nat. Mater., 1 26 –33 (2002). https://doi.org/10.1038/nmat708 Google Scholar

23. 

X. Y. Jiang et al., “An ultrathin terahertz lens with axial long focal depth based on metasurfaces,” Opt. Express, 21 (24), 30030 –30038 (2013). https://doi.org/10.1364/OE.21.030030 OPEXFF 1094-4087 Google Scholar

24. 

J. He et al., “A broadband terahertz ultrathin multi-focus lens,” Sci. Rep., 6 (1), 28800 (2016). https://doi.org/10.1038/srep28800 SRCEC3 2045-2322 Google Scholar

25. 

D. Jia et al., “Transmissive terahertz metalens with full phase control based on a dielectric metasurface,” Opt. Lett., 42 (21), 4494 –4497 (2017). https://doi.org/10.1364/OL.42.004494 OPLEDP 0146-9592 Google Scholar

26. 

W. T. Chen et al., “A broadband achromatic metalens for focusing and imaging in the visible,” Nat. Nanotechnol., 13 (3), 220 –226 (2018). https://doi.org/10.1038/s41565-017-0034-6 NNAABX 1748-3387 Google Scholar

27. 

Z. B. Fan et al., “A broadband achromatic metalens array for integral imaging in the visible,” Light Sci. Appl., 8 67 (2019). https://doi.org/10.1038/s41377-019-0178-2 Google Scholar

28. 

S. Wang et al., “A broadband achromatic metalens in the visible,” Nat. Nanotechnol., 13 227 –232 (2018). https://doi.org/10.1038/s41565-017-0052-4 NNAABX 1748-3387 Google Scholar

29. 

S. M. Wang et al., “Broadband achromatic optical metasurface devices,” Nat. Commun., 8 187 (2017). https://doi.org/10.1038/s41467-017-00166-7 NCAOBW 2041-1723 Google Scholar

30. 

R. J. Lin et al., “Achromatic metalens array for full-colour light-field imaging,” Nat. Nanotechnol., 14 (3), 227 –231 (2019). https://doi.org/10.1038/s41565-018-0347-0 NNAABX 1748-3387 Google Scholar

31. 

Q. Cheng et al., “Broadband achromatic metalens in terahertz regime,” Sci. Bull., 64 (20), 1525 –1531 (2019). https://doi.org/10.1016/j.scib.2019.08.004 Google Scholar

32. 

M. Naftaly and R. E. Miles, “Terahertz time-domain spectroscopy for material characterization,” Proc. IEEE, 95 (8), 1658 –1665 (2007). https://doi.org/10.1109/JPROC.2007.898835 IEEPAD 0018-9219 Google Scholar

33. 

B. Ferguson et al., “T-ray computed tomography,” Opt. Lett., 27 (15), 1312 –1314 (2002). https://doi.org/10.1364/OL.27.001312 OPLEDP 0146-9592 Google Scholar

34. 

X. Ni et al., “Ultra-thin, planar, Babinet-inverted plasmonic metalenses,” Light Sci. Appl., 2 e72 (2013). https://doi.org/10.1038/lsa.2013.28 Google Scholar

35. 

C. Chen et al., “Spectral tomographic imaging with aplanatic metalens,” Light Sci. Appl., 8 99 (2019). https://doi.org/10.1038/s41377-019-0208-0 Google Scholar

36. 

A. Arbabi et al., “Dielectric metasurfaces for complete control of phase and polarization with subwavelength spatial resolution and high transmission,” Nat. Nanotechnol., 10 (11), 937 –943 (2015). https://doi.org/10.1038/nnano.2015.186 NNAABX 1748-3387 Google Scholar

37. 

S. Jahani and Z. Jacob, “All-dielectric metamaterials,” Nat. Nanotechnol., 11 (1), 23 –36 (2016). https://doi.org/10.1038/nnano.2015.304 NNAABX 1748-3387 Google Scholar

38. 

Z. X. Shen et al., “Liquid crystal tunable terahertz lens with spin-selected focusing property,” Opt. Express, 27 (6), 8800 –8807 (2019). https://doi.org/10.1364/OE.27.008800 OPEXFF 1094-4087 Google Scholar

39. 

L. Wang et al., “Broadband tunable liquid crystal terahertz waveplates driven with porous graphene electrodes,” Light Sci. Appl., 4 e253 (2015). https://doi.org/10.1038/lsa.2015.26 Google Scholar

40. 

A. Arbabi et al., “Subwavelength-thick lenses with high numerical apertures and large efficiency based on high-contrast transmitarrays,” Nat. Commun., 6 7069 (2015). https://doi.org/10.1038/ncomms8069 NCAOBW 2041-1723 Google Scholar

41. 

M. V. Berry, “The adiabatic phase and Pancharatnam’s phase for polarized light,” J. Mod. Opt., 34 (11), 1401 –1407 (1987). https://doi.org/10.1080/09500348714551321 JMOPEW 0950-0340 Google Scholar

42. 

P. Chen et al., “Chirality invertible superstructure mediated active planar optics,” Nat. Commun., 10 2518 (2019). https://doi.org/10.1038/s41467-019-10538-w NCAOBW 2041-1723 Google Scholar

43. 

G. Zheng et al., “Metasurface holograms reaching 80% efficiency,” Nat. Nanotechnol., 10 (4), 308 –312 (2015). https://doi.org/10.1038/nnano.2015.2 NNAABX 1748-3387 Google Scholar

44. 

S. Lepeshov et al., “Enhancement of terahertz photoconductive antenna operation by optical nanoantennas,” Laser Photonics Rev., 11 (1), 1600199 (2017). https://doi.org/10.1002/lpor.201600199 Google Scholar

45. 

Z. X. Shen et al., “Liquid-crystal-integrated metadevice: towards active multifunctional terahertz wave manipulations,” Opt. Lett., 43 (19), 4695 –4698 (2018). https://doi.org/10.1364/OL.43.004695 OPLEDP 0146-9592 Google Scholar

46. 

Z. X. Shen et al., “Liquid crystal enabled dynamic cloaking of terahertz Fano resonators,” Appl. Phys. Lett., 114 (4), 041106 (2019). https://doi.org/10.1063/1.5082224 APPLAB 0003-6951 Google Scholar

47. 

P. Chen et al., “Digitalizing self-assembled chiral superstructures for optical vortex processing,” Adv. Mater., 30 (10), 1705865 (2018). https://doi.org/10.1002/adma.201705865 ADVMEW 0935-9648 Google Scholar

48. 

Z. X. Shen et al., “Planar terahertz photonics mediated by liquid crystal polymers,” Adv. Opt. Mater., 8 1902124 (2020). https://doi.org/10.1002/adom.201902124 2195-1071 Google Scholar

49. 

L. Wang et al., “Large birefringence liquid crystal material in terahertz range,” Opt. Mater. Express, 2 (10), 1314 –1319 (2012). https://doi.org/10.1364/OME.2.001314 Google Scholar

50. 

N. Yu et al., “Light propagation with phase discontinuities: generalized laws of reflection and refraction,” Science, 334 (6054), 333 –337 (2011). https://doi.org/10.1126/science.1210713 SCIEAS 0036-8075 Google Scholar

51. 

S. M. Kamali et al., “Decoupling optical function and geometrical form using conformal flexible dielectric metasurfaces,” Nat. Commun., 7 11618 (2016). https://doi.org/10.1038/ncomms11618 NCAOBW 2041-1723 Google Scholar

Biography

Zhixiong Shen received his BEng degree in material physics from Nanjing University, Nanjing, China, in 2016. Currently, he is a PhD student at the College of Engineering and Applied Sciences, Nanjing University. His research interests include liquid crystal terahertz modulators and tunable metamaterials.

Wei Hu received his PhD from Jilin University, Changchun, China, in 2009. Currently, he is a professor at the College of Engineering and Applied Sciences, Nanjing University. His research interests include liquid crystal materials and optical devices.

Yanqing Lu received his PhD from Nanjing University, Nanjing, China, in 1996. Currently, he is a professor at the College of Engineering and Applied Sciences, Nanjing University. His research interests include nonlinear and quantum photonics and liquid crystal devices.

Biographies of the other authors are not available.

© The Authors. Published by SPIE and CLP under a Creative Commons Attribution 4.0 Unported License. Distribution or reproduction of this work in whole or in part requires full attribution of the original publication, including its DOI.
Zhixiong Shen, Shenghang Zhou, Xinan Li, Shijun Ge, Peng Chen, Wei Hu, and Yanqing Lu "Liquid crystal integrated metalens with tunable chromatic aberration," Advanced Photonics 2(3), 036002 (12 May 2020). https://doi.org/10.1117/1.AP.2.3.036002
Received: 3 April 2020; Accepted: 29 April 2020; Published: 12 May 2020
JOURNAL ARTICLE
7 PAGES


SHARE
Advertisement
Advertisement
Back to Top