1 March 2010 Gold nanorods for fluorescence lifetime imaging in biology
Author Affiliations +
Two-photon luminescence (TPL) from gold nanorods shows considerable potential in biological imaging. We study the imaging of gold nanorods in Madin-Darby canine kidney (MDCK) cells using fluorescence lifetime imaging microscopy (FLIM). FLIM provides images with better contrast and sensitivity than intensity imaging. The characteristic fluorescence lifetime of gold nanorods is found to be less than 100 ps, which can be used to distinguish gold nanorods from other fluorescent labels and endogenous fluorophores in lifetime imaging.

Gold nanorods are of great interest for optical imaging due to their remarkable absorption and scattering in the visible and near-infrared (NIR) regions enhanced by surface plasmon resonance (SPR).1, 2 NIR band absorption between 700 and 900nm , a spectral window that permits photons to penetrate biological tissues with relatively high transmission, induces two-photon luminescence with strong intensity.3, 4 Two-photon luminescence (TPL) from gold nanorods has been found to be sensitive to the polarization of the incident excitation.4, 5 All these properties make gold nanorods attractive probes for in-vitro and in-vivo imaging.4, 6, 7 But so far, most related work has utilized traditional microscopy methods such as confocal microscopy and near-field optical microscopy imaging.8, 9, 10, 11, 12

In contrast to traditional imaging methods based on fluorescence intensity, fluorescence lifetime imaging microscopy (FLIM) provides contrast according to the fluorescence decay time, with the term “fluorescence” usually being associated with aromatic dye molecules. Here we have an inorganic system for which the term “luminescence” is usually applied. Lifetime imaging can be integrated with confocal microscopy, two-photon excitation microscopy, and other microscope systems. The luminescence (or fluorescence) decay time is the average time a fluorophore remains in the excited state after excitation. It does not change on intensity variations, and therefore lifetime measurements are not dependent on the local concentration of fluorophores, bleaching, the optical path of the microscope, the local excitation light intensity, or on the local luminescence detection efficiency. Also, the fluorescence decay time for aromatic molecules usually depends usefully on the intrinsic characteristics of the fluorophore and local environment (the local viscosity, pH, or refractive index13, 14, 15) as well as interactions with other molecules, such as collisional or energy transfer quenching.16, 17 Thus, as well as being able to distinguish spectrally overlapping fluorophores,18 imaging of the fluorescence lifetime can be used to probe the surroundings and dynamical processes of a fluorophore.19, 20 Unlike electron microscopy, fluorescence/luminescence techniques can be used in situ.

In this work, we use FLIM to visualize gold nanorods taken up by Madin-Darby canine kidney (MDCK) cells. A very short luminescence decay time of TPL from gold nanorods is observed. Compared with the lifetime of 4-6 -diamidino-2-phenylindole (DAPI), which is more than 2ns , lifetime imaging shows good contrast. Furthermore, besides emission, the lifetime could be an alternative identification of gold nanorods in biological imaging.

Gold nanorods were synthesized by the seeded growth method.21 2.5-ml HAuCl4×3H2O (0.001M) and 0.6-ml ice-cold NaBH4 (0.01M) were added into 7.5-ml cetyltrimethylammonium bromide (CTAB) (0.1M) to prepare the seed solution. The growth solution was synthesized by adding 0.15-M benzyldimethylammoniumchloride (BDAC), 50-ml HAuCl4×3H2O (0.001M) , 2-ml AgNO3 (0.004M) , and 700-μl ascorbic acid (0.778M) to 50-ml CTAB solution (0.1M) . Then 80-μl seed solution ( 2h after preparation) was injected into growth solution to grow gold nanorods. The absorption spectrum shows a longitudinal plasmon mode centered at around 750nm , and a weak transverse plasmon mode at 550nm .

Gold nanorod dispersions were centrifuged to remove the excess CTAB and redispersed in deionized water twice ( 14,000rpm , 5minpercycle ) with a final optical density about 1.0 at 750nm . MDCK cells were treated with 100μl of gold nanorod solution and incubated for 3h under standard cell culture conditions at 37°C and 5% CO2 . The cells were washed thoroughly with phosphate buffered saline (PBS) to remove excess nanorods and fixed with 3.7% paraformaldehyde. After staining with DAPI, the sample was dispersed on a glass slide and covered with a coverslip for imaging.

FLIM was performed by using a confocal microscope (LSM 510, Carl Zeiss) equipped with a time-correlated single-photon counting (TCSPC) module (SPC-830, Becker and Hickl GmbH, Berlin, Germany). A femtosecond Ti:sapphire laser (Chameleon, Coherent, Santa Clara, California) was tuned at 750nm to generate TPL from gold nanorods as well as DAPI. The laser pulse has a repetition rate of 80MHz and a duration of less than 200fs . Emission was collected by a 60× water-immersion objective (NA=1.0) and a bandpass filter with a transmission window from 535to590nm .

Gold nanorods were examined prior to the cell uptake experiment. The pseudocolor TPL image of separated gold nanorods on a glass slide is shown in Fig. 1 , with brighter spots considered to be clusters of nanorods. Furthermore, strong luminescence and a quadratic dependence on the incidence power were observed in a spectroscopy study of gold nanorods in bulk solution. The nonlinear property of the luminescence was studied by measuring the luminescence intensity as a function of excitation power. Luminescence was collected while increasing incident pulse power from 6to20mW . Figure 1 shows a typical result. A quadratic dependence of the signal intensity on the input power confirmed the luminescence originating from a two-photon excitation process.

Fig. 1

(a) TPL image of gold nanorods dispersed on a glass slide, with a scanning area 133×133μm . (b) Dependence of luminescence intensity on incidence laser power (in log scale).


Figure 2 compares the intensity and lifetime imaging of gold nanorods in cells. The elliptical shapes in Figs. 2 and 2 correspond to nuclei stained by DAPI (emission maximizes at around 460nm and does not shift much under two photon excitation22), and bright spots are due to gold nanorods. Internalization of CTAB stabilized gold nanorods in cells has been reported before and studied using 3-D stack confocal microscopy.8, 9 Here, compared with the cell reference sample [Fig. 2], the luminescence intensity image shows that most nanorods were around DAPI dyed nuclei of MDCK cells, and that the nanorods have a stable and strong luminescence intensity. Figure 2 is a FLIM image from the same sample area as in Fig. 2, with different coded colors representing different lifetime scales. The luminescence lifetime of each pixel is obtained by applying a single or multiexponential fit; in this case a single exponential model was used. The fluorescence lifetime of DAPI is found to be longer than 2ns and fitted well by a single exponential model. This value is in accordance with published data on FLIM analysis of DAPI.12 The TPL decay time of gold nanorods is shorter than 100ps ; this result is confirmed by FLIM study of pure gold nanorods on a glass slide, as well as time-resolved luminescence measurement of gold nanorods in a cuvette using the same excitation and time-correlated single-photon counting (TCSPC)23 (not shown here). This value is much longer than those achieved in pump-probe and up-conversion research, where the lifetime of excited electrons in gold nanorods was found to be less than several picoseconds.9, 24, 25 This is probably due to the limit of time resolution caused by the instrumental response function of the TCSPC system, which is also around 100ps . Our measurements thus give the upper limit of the decay time of the TPL process. The lifetime of TPL from large gold nanorods was reported to be 0.8to2.0ns , depending on the shape and size of the particles and also on the detection wavelength, but the details are not clear.5 Therefore, further research is required to reveal the full information of the dynamics of the TPL process in gold nanorods. Nevertheless, the contrast in lifetime scale can be clearly seen in Fig. 2, which gives the typical line shapes of fluorescence decay curves of DAPI (black) and gold nanorods (red), as shown in Fig. 2. The luminescence lifetime distribution of all the pixels is shown in Fig. 2, where two peaks can be identified, one at around 100ps corresponding to gold nanorods, and the other to DAPI.

Fig. 2

(a) Intensity image of reference MDCK cells; (b) TPL intensity and (c) lifetime image of gold nanorods in MDCK cells; (d) typical TPL decay curves of DAPI and gold nanorods; (e) histogram of lifetime of every single pixel in the FLIM image; (f) enlarged lifetime image corresponding to the red rectangular area in (c); and (g) decay curves and fittings derived from regions A, B, and C in (f). Scanning area: 133×133μm for (a), and 67×67μm for (b).


The FLIM image is in good accord with the intensity image, but is superior in contrast to the latter, which is caused by the huge gap between the decay time from the gold nanorods and DAPI. As the lifetime of gold nanorods is much shorter than that of commonly used fluorescent molecules and other quantum particles, the lifetime can be a useful identification parameter in bioimaging. Moreover, FLIM provides details that are lost when using traditional imaging due to the low luminescence intensity, because lifetime measurement does not depend on the fluorophore concentration. For example, detailed features from gold nanorods in the rectangular region in the FLIM image, Fig. 2, are apparent but not visible in the intensity image, Fig. 2. Further investigation on the dynamics of the TPL of gold nanorods and the influence of size and shape of the nanoparticles on the luminescence decay processes are underway.

FLIM can also provide more information based on luminescence lifetime analysis. Figure 2 amplifies the red rectangular region in Fig. 2. In the nuclei areas, orange dots and yellow areas are clearly visible surrounded by blue areas (DAPI). Three typical regions are labeled as A, B, and C. Corresponding decay curves of these three regions derived from the FLIM image are shown in Fig. 2, together with monoexponential (C) or biexponential (B) fittings. Typically, DAPI has a long lifetime in the range of 1.5to3.5ns , such as that found in region C. In contrast, the decay curve in region A is in the system response level, similar to that from separated gold nanorods, indicating a lifetime shorter than 100ps . The decay curve from region B, which can be well fitted by a biexponential model with one component around 100ps and the other at 3ns , are considered to be an overlay of the emissions of nanorods and DAPI. Thus the FLIM image reveals the existence of gold nanorods in these orange-yellow areas, indicating the uptake of gold nanorods by MDCK cells.

In summary, we have studied gold nanorods as luminescence labels in MDCK cells by FLIM, which provides a better contrast ratio and more detailed features than with intensity imaging. The luminescence lifetime of gold nanorods is found to be less than 100ps , much shorter than most dye molecules, suggesting the possibility of distinguishing gold nanorods from extrinsic and endogenous fluorophores in biological systems. Thus, the characteristic lifetime, together with the polarization of TPL from gold nanorods, can be a promising imaging contrast agent for use in luminescence microscopy in biology.


The authors acknowledge J. Sutter for assistance during the experimental work. This work was supported by an EPSRC Science and Innovation Award, and a Pump Priming Award from SPIBS University of Strathclyde.



S. Link and M. El-Sayed, Int. Rev. Phys. Chem., 19 (3), 409 –453 (2000). 0144-235X Google Scholar


M. B. Mohamed, V. Volkov, S. Link, and M. A. El-Sayed, Chem. Phys. Lett., 317 517 –523 (2000). 0009-2614 Google Scholar


R. A. Farrer, F. L. Butterfield, V. W. Chen, and J. T. Fourkas, Nano Lett., 5 (6), 1139 –1142 (2005). 1530-6984 Google Scholar


H. Wang, T. B. Huff, D. A. Zweifel, W. He, P. S. Low, A. Wei, and J. Cheng, Proc. Natl. Acad. Sci. U.S.A., 102 (44), 15752 –15756 (2005). 0027-8424 Google Scholar


K. Imura, T. Nagahara, and H. M. Okamoto, J. Phys. Chem. B, 109 (27), 13214 –13220 (2005). 1089-5647 Google Scholar


X. H. Huang, I. H. El-Sayed, W. Qian, and M. A. El-Sayed, J. Am. Chem. Soc., 128 (6), 2115 –2120 (2006). 0002-7863 Google Scholar


H. Ding, K. T. Yong, I. Roy, H. E. Pudavar, W. C. Law, E. J. Bergey, and P. N. Prasad, J. Phys. Chem. C, 111 (34), 12552 –12557 (2007). 1932-7447 Google Scholar


T. B. Huff, M. N. Hansen, Y. Zhao, J. Cheng, and A. Wei, Langmuir, 23 1596 –1599 (2007). 0743-7463 Google Scholar


T. B. Huff, M. N. Hansen, Y. Zhao, J. Cheng, and A. Wei, Nanomed., 2 125 –132 (2007). Google Scholar


N. J. Durr, T. Larson, D. K. Smith, B. A. Korgel, K. Sokolov, and A. Ben-Yakar, Nano Lett., 7 (4), 941 –945 (2007). 1530-6984 Google Scholar


K. Imura, T. Nagahara, and H. M. Okamoto, J. Phys. Chem. B, 108 16344 –16347 (2004). 1089-5647 Google Scholar


L. Tong, Q. Wei, A. Wei, and J. Cheng, Photochem. Photobiol., 85 21 –32 (2009). 0031-8655 Google Scholar


S. T. Hess, E. D. Sheets, A. Wagenknecht-Wiesner, and A. A. Heikal, Biophys. J., 85 2566 –2580 (2003). 0006-3495 Google Scholar


B. Wilhelmi, Chem. Phys., 66 351 –355 (1982). 0301-0104 Google Scholar


K. Suhling, P. M. W. French, and D. Phillips, Photobio. Sci., 4 13 –22 (2005). Google Scholar


J. R. Lakowicz, Principles of Fluorescence Spectroscopy, 2nd ed.Kluwer Academic-Plenum Publishers, New York (1999). Google Scholar


B. Valeur, Molecular Fluorescence, Wiley-VCH, New York (2002). Google Scholar


A. Rück, C. H. Hülshoff, I. Kinzler, W. Becker, and R. Steiner, Microsc. Res. Tech., 70 485 –492 (2007). 1059-910X Google Scholar


T. Ng, A. Squire, G. Hansra, F. Bornancin, C. Prevostel, A. Hanby, W. Harris, D. Barnes, S. Schmidt, H. Mellor, P. I. Bastiaens, and P. J. Parker, Science, 283 2085 –2089 (1999). 0036-8075 Google Scholar


M. Peter and S. M. Ameer-Beg, Biol. Cell, 96 231 –236 (2004). 0248-4900 Google Scholar


J. Murphy, T. K. Sau, A. M. Gole, C. J. Orendorff, J. Gao, L. Gou, S. E. Hunyadi, and T. Li, J. Phys. Chem. B, 109 13857 –13870 (2005). 1089-5647 Google Scholar


F. Bestvater, E. Spiess, G. Stobrawa, M. Hacker, T. Feurer, T. Porwol, U. Berchner-Pfannschmidt, C. Wotzlaw, and H. Acker, J. Microsc., 208 108 –115 (2002). 0022-2720 Google Scholar


A. Volkmer, D. A. Hatrick, and D. J. S. Birch, Meas. Sci. Technol., 8 1339 –49 (1997). 0957-0233 Google Scholar


O. P. Varnavski, M. B. Mohamed, M. A. El-Sayed, and T. Goodson III, J. Phys. Chem. B, 107 3101 –3104 (2003). 1089-5647 Google Scholar


P. Biagioni, M. Celebrano, M. Savoini, G. Grancini, D. Brida, S. Mátéfi-Tempfli, M. Mátéfi-Tempfli, L. Duò, B. Hecht, G. Cerullo, and M. Finazzi, Phys. Rev. B, 80 045411 (2009). 0163-1829 Google Scholar
©(2010) Society of Photo-Optical Instrumentation Engineers (SPIE)
Yinan Zhang, Jun Yu, David J. S. Birch, and Yu Chen "Gold nanorods for fluorescence lifetime imaging in biology," Journal of Biomedical Optics 15(2), 020504 (1 March 2010).
Published: 1 March 2010

Back to Top