Effects of damage accumulation on quantum well intermixing by low-energy ion implantation in photonic devices

Martin Chicoine; Alexandre Francois; C. Tavares; S. Chevobbe; Francois Schiettekatte; Vincent Aimez; Jacques Beauvais; Jean Beerens

doi:10.1117/12.543537

15 December 2003 Effects of damage accumulation on quantum well intermixing by low-energy ion implantation in photonic devices

Martin Chicoine, Alexandre Francois, C. Tavares, S. Chevobbe, Francois Schiettekatte, Vincent Aimez, Jacques Beauvais, Jean Beerens

Author Affiliations +

Proceedings Volume 5260, Applications of Photonic Technology 6; (2003) https://doi.org/10.1117/12.543537
Event: Applications of Photonic Technology, 2003, Quebec City, Québec, Canada

Abstract

The surface layer of InP-based quantum well (QW) laser structures were implanted with As or P ions at energies ranging from 200 to 360 keV. The structures were then annealed at temperatures ranging from 650 to 750°C during 120s, allowing the defects created by implantation to diffuse, resulting in intermixing at the barrier-QW interfaces. The consequence of the intermixing is the blue shift of the QW photoluminescence wavelength. The blue shfit was studied as a function of the implantation temperature (25 or 200°C). Implantation-induced damage in the samples was characterized by Rutherford Backscattering in channeling mode (RBS-c) and correlated with the observed blue shift. It is found that blue shift is more efficient at higher implantation temperature, even if the resulting defect concentration is much lower. This is attributed to the diffusion of defects during high-temperature implantation, leading to a larger region containing defects contributing to intermixing. Also, when the implanted dose is too high, no blue shift is observed. This could be due to the formation of defect clusters that inhibit the subsequent diffusion of defects. Finally, the defect creation mechanisms within InP and InGaAs layers are found to have a significant impact on the resulting wavelength blue shift.

Citation Download Citation

Martin Chicoine, Alexandre Francois, C. Tavares, S. Chevobbe, Francois Schiettekatte, Vincent Aimez, Jacques Beauvais, and Jean Beerens "Effects of damage accumulation on quantum well intermixing by low-energy ion implantation in photonic devices", Proc. SPIE 5260, Applications of Photonic Technology 6, (15 December 2003); https://doi.org/10.1117/12.543537

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available